| Insulation extrusion | Core A | Core B | Core C |
| Conductor AWG | 10mm2 (80/0.40mm), Bare Stranded Copper | 2.5mm2 (50/0.25mm), Bare Stranded Copper | 0.5mm2 (16/0.20mm), Bare Stranded Copper |
| Conductor Dia. Nom. | 4.13mm | 2.04mm | 0.92mm |
| Primary Number | 2C | 2C | 2C |
| Insulator | PVC(-40~105ºC) | PVC(-40~105ºC) | PVC(-40~105ºC) |
| Primary O. D. | 5.80±0.20mm | 3.50±0.10mm | 2.10±0.10mm |
| Nom.Thickness | 0.75mm | 0.70mm | 0.60mm |
| Min. Thickness | 0.60mm | 0.56mm | 0.48mm |
| Primary Color Code | A1.black A2.red | B1.black B2.red | C1.black C2.red |
| Twisted O.D.(Ref) | / | / | / |
| Assemble | |
| Filler | PP rope |
| Paper(overlapping,%) | ≥25% |
| Jacket extrusion | |
| Jacket material | PVC |
| Jacket Dia | 14.40±0.30mm |
| Nom. Thickness | 1.00mm |
| Min. Thickness | 0.80mm |
| Surface | |
| Marking | LIYY 2x10+2x2.5+2x0.5qmm |
| Color | Black(RAL 9005) |
| Characteristics | Jacket |
| Tensile Strength before Aging | >=10.3Mpa |
| Elongation before Aging | >=100% |
| Aging Condition | 113ºC x 168 Hrs |
| Tensile Strength after Aging | >=70%of original |
| Elongation after Aging | >=65%of original |
| Max. Conductor DC Resistance | A:1.91(Ω/km) B: 7.98(Ω/km) C: 39(Ω/km) |
| Dielectric Strength | 1.0kV/min AC |
| Rated Temperature | -40~80ºC |
| Rated Voltage | 60V |
| Flammability Test | VW-1 |
| UV Resistance | Reference standard:UL1581-1200 720h |
| Oil Resistance (Insulation) | Reference standard: ISO6722 |
| Short Term Heat Ageing (Insulation) | Reference standard: ISO6722 (125ºC x 240 Hrs, No Crack) |
| Remark | Insulation reference standard (A): FLRY-B Insulation reference standard (B,C): FLY |
| Remark | RoHS & Reach compliant |